ELEGOO PLA-CF Hõõgniit (Must)

ELEGOO PLA-CF Filament (black)

ELEGOO PLA-CF (polylactide doped with carbon fiber) filament combines the ease of printing typical of PLA (polylactide - a plant-derived, biodegradable plastic) with higher mechanical strength. The addition of carbon fiber increases the stiffness of the material and reduces its shrinkage during cooling, resulting in greater dimensional precision. This type of material works well in technical components, housings and prototypes that need to be durable but lightweight.

Accurate and aesthetically pleasing models

The addition of carbon fiber reduces shrinkage and deformation of the material, resulting in precise, well-fitted parts. Printed models have a matte surface and faintly visible layer lines, giving a professional effect without additional processing. The material fits most FDM 3D printers (Fused Deposition Modeling - a technology that applies molten plastic layer by layer).

Printing without problems

The filament has a diameter of 1.75 mm and a dimensional tolerance of ± 0.02 mm, which facilitates even feeding without jams. It is vacuum-packed with a moisture absorber to protect against bubbles and a clogged nozzle. It can be used alone or combined with classic PLA, maintaining high quality prints.

General

ManufacturerELEGOOModel50.203.0464ColorBlackWeight1 kg

Recommended print settings

Drying settings before printing55 ± 5°CAmbient temperature and humidity≤ 50°C, ≤ 20% relative humidity (store with moisture absorber)Nozzle temperature210 - 240°CTable temperature (depending on printer and surface)35 - 65°CType of working surfaceTextured PEI (polyetherimide - a durable, adherent material used as a base for 3D printing) or other compatible surfacePrinting speedLess than 300 mm/s

Physical properties

Density1.24 g/cm³Melting point165°CDeflection temperature under load56°CSoftening temperature (Vicat test)64°C

Mechanical properties

Tensile strength (XY - measured in the horizontal plane of the print, where the material is strongest)39 ± 3 MPaElongation at break (XY)7,5% ± 1,3%Bending strength (XY)78 ± 2 MPaBending modulus (XY)3341 ± 172 MPaImpact strength (XY)24.7 ± 1.5 kJ/m²